Semiconductor memory device and method for fabricating the same

ABSTRACT

A semiconductor memory device has a memory region which is formed on a semiconductor substrate and in which a plurality of memory cells each including a memory transistor are arranged as a matrix using a plurality of impurity diffusion layers (bit lines) and a plurality of gate electrodes (word lines) intersecting each other. The gate electrode of each of the memory transistors has an upper surface thereof formed into a protruding portion which is higher in level at the middle portion than at the edge portions. A silicide layer is formed on the upper surface of the protruding portion of the gate electrode of each of the memory transistors.

CROSS-REFERENCE TO RELATED APPLICATIONS

The teachings of Japanese Patent Application JP 2004-219607, filed Jul.28, 2004, are entirely incorporated herein by reference, inclusive ofthe claims, specification, and drawings.

BACKGROUND OF THE INVENTION

The present invention relates to a semiconductor memory device and amethod for fabricating the same and, more particularly, to asemiconductor memory device in which a logic region and a memory regionhaving a diffusion wiring layer structure are embedded and to a methodfor fabricating the same.

As an electrically writable nonvolatile memory device, there has beenknown a semiconductor memory device having a structure (virtual groundsystem) in which a diffusion wiring layer using an impurity diffusionlayer formed in a semiconductor substrate as wiring also serves as thesource region or drain of a memory transistor.

As ultra-miniaturization, higher integration, higher performance, andhigher reliability has been required of semiconductor memory devices inrecent years, the semiconductor memory device having the virtual groundsystem described above has also been required to operate at a higherspeed.

A conventional semiconductor memory device in which a memory regionhaving the virtual ground system and a logic region are embedded isdisclosed in, e.g., Japanese Laid-Open Patent Publication No.2003-347511.

As shown in FIG. 2 in the patent publication mentioned above, a silicidelayer 109 has been formed by using a salicide technology on the uppersurface of the memory gate electrode 105 in a first active region 101 asthe memory region, while a silicide layer 115 has been formed by usingthe salicide technology on the upper surface of each of a logic gateelectrode 112 and an impurity diffusion layer 114 in a second activeregion 102 as the logic region.

However, as the miniaturization of a semiconductor device proceeds anddesign rules are reduced increasingly, the width of the gate electrodein the memory region is also reduced. Accordingly, a resistance valueper unit length of the gate electrode (bar resistance) increases inproportion to the reciprocal of the gate width so that a resistancevalue per unit length (bar resistance) in a 0.1 μm process becomes tentimes the resistance value per unit length in a 1 μm process. Even in astructure in which the upper surface of the gate electrode has beensilicidized as in the conventional embodiment, a resistance value perunit length of a gate electrode (bar resistance) increases in proportionto the reciprocal of the gate width. If wires are further thinned,therefore, the structure in which the upper surface of the gateelectrode is silicidized leads to the problem that it cannot satisfyboth of the requirement for the ultra-miniaturization of a semiconductordevice and the requirement for the higher-speed operation thereof. In agate electrode in the virtual ground system, the dimension of the gateelectrode perpendicular to the direction in which the gate electrodeextends is termed the gate width.

SUMMARY OF THE INVENTION

In view of the conventional problem described above, it is therefore anobject of the present invention to further reduce a gate resistancevalue under the trend toward a further reduction in the size of a gateelectrode or the like in a semiconductor memory device.

To attain the object, the present invention provides a semiconductormemory device with a structure in which the gate electrode of atransistor composing a memory cell is formed to have an upper portionwhich is configured to protrude upward at the middle portion thereofsuch that the contact area between the gate electrode and a silicidelayer formed on the upper surface of the gate electrode is increased.

Specifically, a semiconductor memory device according to the presentinvention is a semiconductor memory device having a memory region inwhich a plurality of memory cells each including a memory transistor arearranged as a matrix using a plurality of bit lines and a plurality ofword lines intersecting each other, wherein a gate electrode of each ofthe memory transistors has an upper surface thereof formed into aprotruding portion which is higher in level at a middle portion than atan edge portion and a silicide layer is formed on an upper surface ofthe protruding portion of the gate electrode of the memory transistor.

In the semiconductor memory device according to the present invention,the silicide layer formed on the upper surface of the gate electrode hasa length therealong in the gate width direction which is larger thanwhen the upper surface of the gate electrode is flat. The arrangementincreases the contact area between the main body of the gate electrodeand the silicide layer formed on the upper surface thereof and reducesthe resistance value per unit length of the gate electrode (barresistance). As a result, the memory transistor can satisfy therequirements for further miniaturization and higher-speed operation.

In the semiconductor memory device according to the present invention,each of the memory transistors preferably has an impurity diffusionlayer serving as a source region or drain region and also constituting apart of the corresponding one of the bit lines and has the gateelectrode constituting a part of the corresponding one of the wordlines. The arrangement can implement a virtual ground system in which adiffusion wiring layer using an impurity diffusion layer as wiring alsoserves as the source or drain of a memory transistor.

In this case, an inter-gate insulating film is preferably formed on aregion of the substrate which is located between the respective gateelectrodes of the plurality of memory transistors. The arrangement canprevent, during the formation of the silicide layer, a short circuitbetween the adjacent impurity diffusion layers (bit lines) due to thesilicide layer.

Preferably, the semiconductor memory device according to the presentinvention further has: a logic region formed on a region of thesubstrate other than the memory region and in which a logic transistoris disposed, wherein a sidewall insulating film is formed on each sidesurface of a gate electrode of the logic transistor.

In this case, a silicide layer is preferably formed on each of an uppersurface of the gate electrode of the logic transistor and an exposedportion of an impurity diffusion layer serving as a source region ordrain region of the logic transistor. The arrangement reduces theresistance value of each of the upper surface of the gate electrode andthe source region or drain region even in the logic region and therebyallows higher-speed operation of the logic region.

In the semiconductor memory device according to the present invention, amemory gate insulating film formed under the gate electrode of each ofthe memory transistors preferably has a charge accumulation film. Thearrangement can implement a semiconductor memory element which allowsthe accumulation of charge in the memory gate insulating film.

In this case, the memory gate insulating film is preferably composed ofa multilayer structure having a lower-layer silicon oxide film and anupper-layer silicon nitride film and the charge accumulation film ispreferably composed of the upper-layer silicon nitride film.

Alternatively, in this case, the memory gate insulating film ispreferably composed of a multilayer structure having a lower-layersilicon oxide film, an intermediate-layer silicon nitride film, and anupper-layer silicon oxide film and the charge accumulation film ispreferably composed of the intermediate-layer silicon nitride film.

In the semiconductor memory device according to the present invention,the memory gate insulating film formed under the gate electrode of eachof the memory transistors is preferably composed of a multilayerstructure having a lower-layer silicon oxide film, an intermediate-layersilicon nitride film, and an upper-layer silicon oxide film and theintermediate-layer silicon nitride film is preferably formed as a commonintermediate-layer silicon nitride film connecting the respective memorygate insulating films of the plurality of memory transistors to eachother. The arrangement can prevent the silicide layer from being formedon the upper surface of the impurity diffusion layer since the impuritydiffusion layer is less likely to be exposed even when an over-etchedstate is reached during the formation of the inter-gate insulating film.

In the semiconductor memory device according to the present invention,of the plurality of memory transistors, each pair adjacent to each otherin a direction in which each of the word lines extends preferably sharethe common impurity diffusion layer serving as the source region of oneof the adjacent pair of memory transistors and also as the drain regionof the other thereof. The arrangement can reduce the area of each of thememory cells advantageously for higher integration.

In the semiconductor memory device according to the present invention,when the silicide layer has been formed on each of the upper surface ofthe gate electrode of the logic transistor and the exposed portion ofthe impurity diffusion layer serving as the source region or drainregion, the silicide layer on the gate electrode of each of the memorytransistors and the silicide layer on the gate electrode of the logictransistor preferably have different cross-sectional configurations in adirection perpendicular to a surface of the substrate.

A first method for fabricating a semiconductor device according to thepresent invention is a method for fabricating a semiconductor memorydevice having a memory region in which a plurality of memory cells eachincluding a memory transistor are arranged as a matrix using a pluralityof bit lines and a plurality of word lines intersecting each other and alogic region in which a logic transistor is disposed, the methodcomprising the steps of: forming, in the memory region, a first commonimpurity diffusion layer serving as a source region or drain region ofeach of the memory transistors composing those of the plurality ofmemory cells which are arranged in a direction in which each of the bitlines extends such that the first common impurity diffusion layerextends in the direction in which the bit line extends; forming a memorygate insulating film on the memory region of the substrate, whileforming a logic gate insulating film on the logic region of thesubstrate; depositing a silicon-containing film on each of the memorygate insulating film and the logic gate insulating film; patterning thesilicon-containing film in the memory region to form the common gateelectrode of those of the plurality of memory transistors which arearranged in a direction in which each of the word lines extends suchthat the common gate electrode extends in the direction in which theword line extends, while patterning the silicon-containing film in thelogic region to form the gate electrode of the logic transistor; forminga sidewall insulating film on each side surface of the gate electrode ofthe logic transistor; forming, in the logic region, a second impuritydiffusion layer serving as a source region or drain region of the logictransistor; forming a first insulating film on each of the memory regionand the logic region and then forming a second insulating film having acomposition different from a composition of the first insulating film onthe first insulating film that has been formed; successively performingetching with respect to the second insulating film and the firstinsulating film in the memory region to expose an edge portion of anupper surface of the gate electrode of each of the plurality of memorytransistors; after exposing the edge portion of the upper surface of thegate electrode of each of the plurality of memory transistors, furtherperforming etching to expose the upper surface of the gate electrode ofeach of the plurality of memory transistors and remove the edge portionof the upper surface of the gate electrode, while forming an inter-gateinsulating film composed at least of the first insulating film betweenthe respective gate electrodes of those of the memory transistors whichare adjacent to each other in the direction in which each of the bitlines extends; successively performing etching with respect to thesecond insulating film and the first insulating film in the logic regionto expose each of an upper surface of the gate electrode of the logictransistor and an upper surface of the second impurity diffusion layer;and forming a silicide layer on each of the upper surface of the gateelectrode of each of the plurality of memory transistors from which theedge portion has been removed, the upper surface of the gate electrodeof the logic transistor, and an exposed portion of the second impuritydiffusion layer.

Since the first method for fabricating a semiconductor memory deviceremoves the edge portion of the upper surface of the gate electrode ofeach of the memory transistors, the upper surface of the gate electrodeof the memory transistor can be formed into a protruding portion whichis higher in level at the middle portion than at the edge portions.Accordingly, the silicide layer having a large contact area can beformed on the upper surface of the gate electrode of each of the memorytransistors in the subsequent silicidization step. As a result, theresistance value per unit length of each of the gate electrode (barresistance) of each of the memory transistors is reduced and the memorytransistor can satisfy the requirements for further miniaturization andhigher-speed operation. Since the first and second insulating filmshaving different compositions, i.e., different etching resistances areused for an insulating film filling the spaces between the respectivegate electrodes of the memory transistors, the insulating film can bedeposited to a desired thickness between the gate electrodes of thememory transistors by adjusting the thickness of each of the first andsecond insulating films, irrespective of the magnitude of the spacingbetween the gate electrodes. Since it is necessary to expose the secondimpurity diffusion layer for silicidization in the logic region,compositions which allow easy removal of the first and second insulatingfilms can be selected therefor.

In the first method for fabricating a semiconductor memory device, thememory gate insulating film preferably has a charge accumulation film.

In this case, the memory gate insulating film is preferably composed ofa multilayer structure having a lower-layer silicon oxide film and anupper-layer silicon nitride film and the charge accumulation film ispreferably composed of the upper-layer silicon nitride film.

In this case, the memory gate insulating film is preferably composed ofa multilayer structure having a lower-layer silicon oxide film, anintermediate-layer silicon nitride film, and an upper-layer siliconoxide film and the charge accumulation film is preferably composed ofthe intermediate-layer silicon nitride film.

In the first method for fabricating a semiconductor memory device, theetching performed with respect to the second and first insulating filmsin the step of exposing the edge portion of the upper surface of thegate electrode of each of the plurality of memory transistors ispreferably isotropic etching. The arrangement allows easy exposure ofonly the edge portion of the gate electrode of each of the memorytransistors.

In the first method for fabricating a semiconductor memory device, theetching performed with respect to the second and first insulating filmsafter exposing the edge portion of the upper surface of the gateelectrode of each of the plurality of memory transistors is preferablyanisotropic etching. The arrangement allows easier formation of theinter-gate insulating film composed at least of the first insulatingfilm between the respective gate electrodes of the memory transistors.

In the first method for fabricating a semiconductor memory device, theetching of the second and first insulating films is preferably performedunder such a condition that an etch rate for each of the first andsecond insulating films is higher than an etch rate for thesilicon-containing film. The arrangement can prevent the edge portion ofthe gate electrode of each of the memory transistors from beingover-etched.

In the first method for fabricating a semiconductor memory device, thesecond insulating film is preferably formed by reverse sputtering. Thearrangement allows the portion of the second insulating film overlyingthe gate electrode of each of the memory transistors to be formed intoan upwardly protruding configuration and thereby allows easy exposure ofonly the edge portion of the gate electrode of each of the memorytransistors.

A second method for fabricating a semiconductor memory device is amethod for fabricating a semiconductor memory device having a memoryregion in which a plurality of memory cells each including a memorytransistor are arranged as a matrix using a plurality of bit lines and aplurality of word lines intersecting each other and a logic region inwhich a logic transistor is disposed, the method comprising the stepsof: forming, in the memory region, a first common impurity diffusionlayer serving as a source region or drain region of each of the memorytransistors composing those of the plurality of memory cells which arearranged in a direction in which each of the bit lines extends such thatthe first common impurity diffusion layer extends in the direction inwhich the bit line extends; forming a memory gate insulating film on thememory region of the substrate, while forming a logic gate insulatingfilm on the logic region of the substrate; depositing asilicon-containing film on each of the memory gate insulating film andthe logic gate insulating film; patterning the silicon-containing filmin the memory region to form the common gate electrode of those of theplurality of memory transistors which are arranged in a direction inwhich each of the word lines extends such that the common gate electrodeextends in the direction in which the word line extends; forming aninsulating film on each of the memory region and the logic region;performing etching with respect to the insulating film on the memoryregion to expose an edge portion of an upper surface of the gateelectrode of each of the plurality of memory transistors; after exposingthe edge portion of the upper surface of the gate electrode, furtherperforming etching to expose the upper surface of the gate electrode ofeach of the plurality of memory transistors and remove the edge portionof the upper surface of the gate electrode, while forming an inter-gateinsulating film composed of the insulating film between the respectivegate electrodes of those of the memory transistors which are adjacent toeach other in the direction in which each of the bit lines extends;patterning the silicon-containing film in the logic region to form thegate electrode of the logic transistor; forming a sidewall insulatingfilm on each side surface of the gate electrode of the logic transistor;forming, in the logic region, a second impurity diffusion layer servingas a source region or drain region of the logic transistor; and forminga silicide layer on each of the upper surface of the gate electrode ofeach of the plurality of memory transistors from which the edge portionhas been removed, the upper surface of the gate electrode of the logictransistor, and an exposed portion of the second impurity diffusionlayer.

Since the second method for fabricating a semiconductor memory deviceremoves the edge portion of the upper surface of the gate electrode ofeach of the memory transistors, the upper surface of the gate electrodeof the memory transistor can be formed into a protruding portion whichis higher in level at the middle portion than at the edge portion.Accordingly, the silicide layer having a large contact area can beformed on the upper surface of the gate electrode of each of the memorytransistors in the subsequent silicidization step. As a result, theresistance value per unit length of each of the gate electrode (barresistance) of each of the memory transistors is reduced and the memorytransistor can satisfy the requirements for further miniaturization andhigher-speed operation.

In the second method for fabricating a semiconductor memory device, thememory gate insulating film preferably has a charge accumulation film.

In this case, the memory gate insulating film is preferably composed ofa multilayer structure having a lower-layer silicon oxide film and anupper-layer silicon nitride film and the charge accumulation film ispreferably composed of the upper-layer silicon nitride film.

Alternatively, in this case, the memory gate insulating film ispreferably composed of a multilayer structure having a lower-layersilicon oxide film, an intermediate-layer silicon nitride film, and anupper-layer silicon oxide film and the charge accumulation film ispreferably composed of the intermediate-layer silicon nitride film.

In the second method for fabricating a semiconductor memory device, theetching performed with respect to the insulating film in the step ofexposing the edge portion of the upper surface of the gate electrode ofeach of the plurality of memory transistors is preferably isotropicetching.

In the second method for fabricating a semiconductor memory device, theetching performed with respect to the insulating film after exposing theedge portion of the upper surface of the gate electrode of each of theplurality of memory transistors is preferably anisotropic etching.

In the second method for fabricating a semiconductor memory device, theetching of the insulating film is preferably performed under such acondition that an etch rate for the insulating film is higher than anetch rate for the silicon-containing film.

In the second method for fabricating a semiconductor memory device, theinsulating film is preferably formed by reverse sputtering.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a partial plan view showing a semiconductor memory deviceaccording to a first embodiment of the present invention;

FIGS. 2A to 2C show the semiconductor memory device according to thefirst embodiment, of which FIG. 2A is a cross-sectional view taken alongthe line IIa-IIa of FIG. 1, FIG. 2B is a cross-sectional view takenalong the line IIb-IIb of FIG. 1, and FIG. 2C is a cross sectional viewtaken along the line IIc-IIc of FIG. 1;

FIGS. 3A to 3C are cross-sectional views illustrating a process step ofa method for fabricating the semiconductor memory device according tothe first embodiment;

FIGS. 4A to 4C are cross-sectional views illustrating a process step ofthe method for fabricating the semiconductor memory device according tothe first embodiment;

FIGS. 5A to 5C are cross-sectional views illustrating a process step ofthe method for fabricating the semiconductor memory device according tothe first embodiment;

FIGS. 6A to 6C are cross-sectional views illustrating a process step ofthe method for fabricating the semiconductor memory device according tothe first embodiment;

FIGS. 7A to 7C are cross-sectional views illustrating a process step ofthe method for fabricating the semiconductor memory device according tothe first embodiment;

FIGS. 8A to 8C are cross-sectional views illustrating a process step ofthe method for fabricating the semiconductor memory device according tothe first embodiment;

FIGS. 9A to 9C are cross-sectional views illustrating a process step ofthe method for fabricating the semiconductor memory device according tothe first embodiment;

FIGS. 10A to 10C are cross-sectional views illustrating a process stepof the method for fabricating the semiconductor memory device accordingto the first embodiment;

FIGS. 11A to 11C are cross-sectional views illustrating a process stepof a method for fabricating a semiconductor memory device according to afirst variation of the first embodiment;

FIGS. 12A to 12C are cross-sectional views illustrating a process stepof a method for fabricating a semiconductor memory device according to asecond variation of the first embodiment;

FIG. 13 is a partial plan view showing a semiconductor memory deviceaccording to a second embodiment of the present invention;

FIGS. 14A to 14C are cross-sectional views illustrating a process stepof a method for fabricating the semiconductor memory device according tothe second embodiment;

FIGS. 15A to 15C are cross-sectional views illustrating a process stepof the method for fabricating the semiconductor memory device accordingto the second embodiment;

FIGS. 16A to 16C are cross-sectional views illustrating a process stepof the method for fabricating the semiconductor memory device accordingto the second embodiment;

FIGS. 17A to 17C are cross-sectional views illustrating a process stepof the method for fabricating the semiconductor memory device accordingto the second embodiment;

FIGS. 18A to 18C are cross-sectional views illustrating a process stepof the method for fabricating the semiconductor memory device accordingto the second embodiment;

FIGS. 19A to 19C are cross-sectional views illustrating a process stepof the method for fabricating the semiconductor memory device accordingto the second embodiment;

FIGS. 20A to 20C are cross-sectional views illustrating a process stepof a method for fabricating a semiconductor memory device according to afirst variation of the second embodiment; and

FIGS. 21A to 21C are cross-sectional views illustrating a process stepof a method for fabricating a semiconductor memory device according to asecond variation of the second embodiment

DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiment 1

A first embodiment of the present invention will be described withreference to the drawings.

FIG. 1 shows a partial plan configuration of a semiconductor memorydevice according to the first embodiment. FIG. 2A shows across-sectional configuration along the line IIa-IIa of FIG. 1. FIG. 2Bshows a cross-sectional configuration along the line IIb-IIb of FIG. 1.FIG. 2C shows a cross-sectional configuration along the line IIc-IIc ofFIG. 1.

As shown in FIG. 1 and FIGS. 2A to 2C, the semiconductor memory deviceaccording to the first embodiment has a first active region 103 as amemory region in which a plurality of memory cells are provided and asecond active region 104 as a logic region in which a logic element isprovided. The first and second active regions 103 and 104 are isolatedfrom each other by an isolation insulating film 102 formed selectivelyin an upper portion of a semiconductor substrate 101 made of, e.g.,silicon (Si). In the first active region 103, a plurality of memorytransistors are provided as a matrix, while a logic transistor isprovided in the second active region 104.

In the first active region 103, a plurality of memory gate electrodes105 are formed over the principal surface of the semiconductor substrate101 with respective memory gate insulating films 110 interposedtherebetween. Each of the memory gate insulating films 110 is composedof a multilayer structure having a lower gate insulating film 110 a madeof silicon oxide, a charge accumulation film 110 b made of siliconnitride, and an upper gate insulating film 110 c made of silicon oxide,which are formed successively on the principal surface of thesemiconductor substrate 101. On the respective side surfaces of thememory gate insulating films 110 and the memory gate electrodes 105,sidewall insulating films 106 are formed.

A plurality of memory transistors arranged in the gate length directions(the directions in which the gate electrodes 105 extend) have therespective memory gate electrodes 105 which are formed in mutuallyconnected relation to constitute common gate electrodes 105. The commonmemory gate electrodes 105 form individual word lines. The upper surfaceof each of the memory gate electrodes 105 has edge portions (peripheralportions) each processed into a tapered or rounded cross-sectionalconfiguration. Silicide layers 109 are formed on the respectiveprocessed upper surfaces.

Since the gate electrode 105 of each of the memory transistors in thesemiconductor device according to the first embodiment has the upperportion thereof thus processed into the tapered or roundedcross-sectional configuration, the cross-sectional area of each of thesilicide layers 109 in the gate width direction (the directionperpendicular to the direction in which each of the gate electrodes 105extends) is larger than the cross-sectional area in the gate widthdirection of the memory gate electrode according to the conventionalembodiment and than the cross-sectional area in the gate width directionof a silicide layer 117 on the upper portion of a logic gate electrode112 having the same width as each of the memory gate electrodes 105.

For example, when the upper surface of each of the memory gateelectrodes 105 is formed to have edge portions each tapered at angle of450 relative to a normal to a substrate surface and the resultingside-tapered upper surfaces of the memory gate 105 become tangent toeach other at the middle to form an edge line, i.e., when a crosssection of the upper portion of the memory gate electrode 105 in adirection perpendicular to the substrate surface has anisosceles-triangular configuration, the area of the upper surface of thememory gate electrode 105 including the edge portions thereof prior to asilicidization step is about 1.4 times the area thereof when no taperedconfiguration is formed. Consequently, the resistance value of thememory gate electrode 105 after the silicidization becomes about 0.7times the resistance value thereof when no tapered configuration isformed. By thus making the taper angle more acute and increasing thesize of the tapered portion, the resistance value of the memory gateelectrode 105 can be reduced more effectively.

The cross section of the upper portion of the memory gate electrode 105in the direction perpendicular to the substrate surface is not limitedto a tapered configuration or a rounded configuration provided that theupper surface of the memory gate electrode 105 has a protrudingconfiguration which is higher in level at the middle portion than at theedge portions.

In the first active region 103 as the memory region, impurity diffusionlayers 107 are formed to extend in directions orthogonal to thedirections in which the word lines extend. Each of the impuritydiffusion layers 107 is formed to serve as the common source region ordrain region of the memory transistors which are arranged in thedirection orthogonal to the direction in which each of the word linesextends, while connecting the memory transistors to each other. Thesecommon source region or drain regions form bit lines.

Thus, each of the memory transistors is constituted by the memory gateinsulating film 110, the memory gate electrode 105 having the silicidelayer 109 formed on the upper portion thereof, and the impuritydiffusion layers 107. Between the memory gate electrodes 105, memoryinter-gate insulating films 108 are formed.

In the second active region 104 as the logic region, on the other hand,the logic gate electrode 112 is formed over the principal surface of thesemiconductor substrate 101 with a logic gate insulating film 111 madeof silicon oxide interposed therebetween. A sidewall insulating film 113is formed on each of the respective side surfaces of the logic gateinsulating film 111 and the logic gate electrode 112. In the secondactive region 104, the impurity diffusion layers 114 each serving as thesource region or drain region are formed. The silicide layers 117 areformed on the respective upper surfaces of the logic gate electrode 112and the impurity diffusion layers 114.

Thus, the logic transistor composed of a field-effect transistor isconstituted by the logic gate insulating film 111, the logic gateelectrode 112 having the silicide layer 117 formed on the upper portionthereof, and the impurity diffusion layers 114 each having the silicidelayer 117 formed on the upper portion thereof.

A method for fabricating the semiconductor memory device according tothe first embodiment thus constituted will be described herein belowwith reference to the cross-sectional views of FIGS. 3A to 3C throughFIGS. 10A to 10C which illustrate individual process steps in the orderin which the fabrication process proceeds. Each of FIGS. 3A, 4A, 5A, 6A,7A, 8A, 9A, and 10A shows a cross-sectional configuration of the portioncorresponding to the line IIa-IIa of FIG. 1. Each of FIGS. 3B, 4B, 5B,6B, 7B, 8B, 9B, and 10B shows a cross-sectional configuration of theportion corresponding to the line IIb-IIb of FIG. 1. Each of FIGS. 3C,4C, 5C, 6C, 7C, 8C, 9C, and 10C shows a cross-sectional configuration ofthe portion corresponding to the line IIc-IIc of FIG. 1.

First, as shown in FIGS. 3A, 3B, and 3C, silicon oxide is buried intrenched portions each formed at a depth of about 300 nm in the upperportion of the semiconductor substrate 101 to form the isolationinsulating film 102, whereby the first active region 103 as the memoryregion and the second active region 104 as the logic region are formed.Subsequently, impurity ions, e.g., arsenic ions are implanted at a doseof about 5×10¹⁵/cm² into the specified portions of the first activeregion 103 with an acceleration voltage of about 50 KeV. Then, a thermalprocess in a nitrogen atmosphere at a temperature of, e.g., about 900°C. is performed for about 60 minutes with respect to the semiconductorsubstrate 100 into which the ions have been implanted to activate theimplanted arsenic ions, whereby the plurality of impurity diffusionlayers 107 serving as the source or drain regions of the memorytransistors are formed in the directions in which the bit lines extend.

Next, as shown in FIGS. 4A, 4B, and 4C, a lower-layer silicon oxide filmhaving a thickness of 10 nm is formed by thermal oxidation on each ofthe first and second active regions 103 and 104 of the principal surfaceof the semiconductor substrate 101 and an intermediate-layer siliconnitride film having a thickness of 7 nm and an upper-layer silicon oxidefilm having a thickness of 10 nm are deposited successively on theformed lower-layer silicon oxide film by low-pressure CVD (chemicalvapor deposition). It is to be noted that the upper-layer silicon oxidefilm need not necessarily be formed.

Subsequently, the intermediate-layer silicon oxide film and theupper-layer silicon oxide film are removed selectively from the secondactive region 104 by using a well-known etching technology. Then, apolycrystalline silicon film as a silicon-containing film having athickness of about 200 nm is deposited by low-pressure CVD on each ofthe first and second active regions 103 and 104. Subsequently, impurityions, e.g., phosphorus ions are implanted at a dose of about 2×10¹⁵/cm²into the deposited polycrystalline silicon films with an accelerationvoltage of about 10 KeV. Thereafter, a thermal process in a nitrogenatmosphere at a temperature of, e.g., about 800° C. is performed forabout 15 minutes with respect to the polycrystalline silicon films intowhich the ions have been implanted, thereby activating the implantedphosphorus ions.

Then, in the first active region 103, the polycrystalline silicon film,the upper-layer silicon oxide film, the intermediate-layer siliconnitride film, and the lower-layer silicon oxide film are patternedsuccessively by using well-known lithographic and etching technologiesto form the memory gate electrodes 105 each composed of thepolycrystalline silicon film and the memory gate insulating films 110each constituted by a multilayer structure having the upper gateinsulating film 110 c composed of the upper-layer silicon oxide film,the charge accumulation film 110 b composed of the intermediate-layersilicon nitride film, and the lower silicon oxide film 110 a composed ofthe lower-layer silicon oxide film.

In the second active region 104, on the other hand, the polycrystallinesilicon film and the lower-layer silicon oxide film are patterned byusing lithographic and etching technologies to form the logic gateelectrode 112 composed of the polycrystalline silicon film and the logicgate insulating film 111 composed of the lower-layer silicon oxide film.

Subsequently, in each of the first and second active regions 103 and104, a silicon oxide film having a thickness of about 100 nm isdeposited by low-pressure CVD and an etch-back process corresponding toa depth of about 110 nm is performed with respect to the depositedsilicon oxide film, thereby forming the sidewall insulating films 106 onthe respective side surfaces of the memory gate electrode 105 and thememory gate insulating film 110, while forming the sidewall insulatingfilm 113 on the side surfaces of the logic gate electrode 112.

Subsequently, impurity ions, e.g., arsenic ions are implanted into thesecond active region 104 by using the logic gate electrode 112 and thesidewall insulating film 113 as a mask and then a specified thermalprocess is performed to form the impurity diffusion layers 114 eachserving as the source region or drain region.

Next, as shown in FIGS. 5A, 5B, and 5C, the first insulating film 115composed of a silicon oxide film having a thickness of about 30 nm isdeposited by plasma CVD over the entire surface of the semiconductorsubstrate 101 including the plurality of memory gate electrodes 105, thelogic gate electrode 112, and the isolation insulating film 102 in thefirst and second active regions 103 and 104. Subsequently, a secondinsulating film 116 composed of a BPSG (boron-doped phospho-silicateglass) film having a thickness of about 300 nm and containing aphosphorous impurity at a concentration of 2 wt % and a boron impurityat a concentration of 7 wt % is deposited by atmospheric-pressure CVD onthe deposited first insulating film 115.

Next, as shown in FIGS. 6A, 6B, and 6C, a first resist pattern 118 forexposing the first active region 103 is formed by using a lithographictechnology on the second insulating film 116 and then anisotropicetching including an isotropic etching component is performed withrespect to the second and first insulating films 116 and 115 by usingthe formed first resist pattern 118 as a mask, thereby exposing the edgeportions of the upper surface of each of the memory gate electrodes 105.By way of example, the dry etching including an isotropic etchingcomponent is performed under such conditions that tetra fluorocarbon(CF₄) at a flow rate of 100 cm³/min (at 0° C. and 1 atm) and oxygen (O₂)at a flow rate of 20 cm³/min (at 0° C. and 1 atm) are used as etchinggases, power is adjusted to 100 W, and the pressure in a chamber isadjusted to 50 Pa.

Next, as shown in FIGS. 7A, 7B, and 7C, an etching process is furtherperformed under dry etching conditions including the lower etchingselectivity between the polycrystalline silicon and the first and secondinsulating films 115 and 116 each containing silicon oxide as the maincomponent, thereby exposing the upper surface of each of the memory gateelectrodes 105, while etching each of the edge portions of the uppersurfaces of the memory gate electrodes 105 into a tapered or roundedconfiguration by using an over-etching process. By way of example, thedry etching with the low etching selectivity may be performedappropriately by increasing the flow rate of oxygen among the foregoingetching conditions from 20 cm³/min (at 0° C. and 1 atm) to 50 cm³/min(at 0° C. and 1 atm).

It is to be noted that each of the edge portions of the upper surfacesof the memory gate electrodes 105 is not limited to a tapered or roundedconfiguration provided that etching is performed in such a manner as toform the upper surface of each of the memory gate electrodes 105 into aprotruding portion which is higher in level at the middle portion thanat the edge portions (peripheral portions). By the sequence of etchingsteps also, the first insulating film 115 is left as the memoryinter-gate insulating films 108 on the regions of the principal surfaceof the semiconductor substrate 101 which are located between theplurality of memory gate electrodes 105.

Thus, the fabrication method according to the first embodiment performsanisotropic etching including an isotropic etching component, as shownin FIGS. 6A, 6B, and 6C, and thereby allows the edge portions of theupper surface of each of the memory gate electrodes 105 to be exposedbefore the middle portion thereof is exposed. As a result, the edgeportions of the upper surface of the memory gate electrode 105 areexposed to an etching gas for a longer period than the middle portionthereof, which allows the formation of each of the edge portions of theupper surfaces of the gate electrodes into a tapered or roundedconfiguration. Since at least the first insulating film 115 existsbetween the adjacent memory gate electrodes 105 in the sequence ofetching steps, the regions of the semiconductor substrate 101 which arelocated between the memory gate electrodes 105 are prevented from beinggrated by etching. Moreover, since the second active region 104 iscovered with the first resist pattern 118 in the sequence of etchingsteps, the portion of the semiconductor substrate 101 included in thesecond active region 104, the isolation insulating film 102, and thelogic gate electrode 112 are prevented from being grated by etching.

Next, as shown in FIGS. 8A, 8B, and 8C, the first resist pattern 118 isremoved and then the second insulating film 116 is removed by wetetching using a diluted hydrofluoric acid solution. As a result, thesecond insulating film 116 remaining between the memory gate electrodes105 is substantially removed from the first active region 103 so thatthe memory inter-gate insulating film 108 composed of the firstinsulating film 115 is formed. The second insulating film 116 is alsosubstantially removed from the second active region 104 so that thefirst insulating film remains.

Next, as shown in FIGS. 9A, 9B, and 9C, a second resist pattern 119 forexposing the second active region 104 is formed by using a lithographictechnology on the semiconductor substrate 101. Then, wet etching using adiluted hydrofluoric acid solution is performed with respect to thefirst insulating film 115 by using the formed second resist pattern 119as a mask to remove the first insulating film 115 remaining in thesecond active region 104, thereby exposing the respective upper surfacesof the logic gate electrode 112 and the impurity diffusion layer 114.

Next, as shown in FIGS. 10A, 10B, and 10C, the silicide layer 109 isformed by using a salicide technology on the tapered or rounded uppersurface as the protruding portion of each of the memory gate electrodes105 including the edge portions in the first active region 103. At thesame time, the silicide layer 117 is formed on each of the upper surfaceof the logic gate electrode 112 and the upper surface of the impuritydiffusion layer 114 in the second active region 104.

By the process described above, the semiconductor memory deviceaccording to the first embodiment can be obtained. Since a metal wiringstep, a protection-film forming step, a bonding-pad forming step, andthe like which are performed subsequently are well known, thedescription thereof will be omitted.

As described above, the first embodiment allows easy formation of thesilicide layer 109 on each of the memory gate electrodes 105 such thatthe length of the silicide layer 109 in the gate width direction islarger than the width of the gate by forming the upper surface of eachof the memory gate electrodes 105 into the protruding portion having theupwardly protruding middle portion in the first active region 103 as thememory region and then forming the silicide layer 109 on the protrudingportion. As a result, the contact area of the silicide layer 109 perunit length of the gate electrode increases and the resistance value perunit length of the memory gate electrode 105 (bar resistance) can bereduced. This allows the memory transistor to satisfy the requirementsfor further miniaturization and higher-speed operation.

Variation 1 of Embodiment 1

Referring to FIGS. 11A to 11C, a description will be given herein belowto a method for fabricating a semiconductor memory device according to afirst variation of the first embodiment of the present invention.

In contrast to the fabrication method according to the first embodimentwhich has used the anisotropic dry etching process including anisotropic etching component as the etching process for selectivelyexposing the edge portions of the upper surface of each of the memorygate electrodes 105 shown in FIGS. 6A to 6C, the first variationperforms isotropic etching and thereby forms the second insulating film116 such that it is thinner at the portions thereof in the vicinity ofthe edge portions of the upper surface of the memory gate electrode 105than at the middle portion thereof.

Specifically, as shown in FIGS. 11A, 11B, and 11C, wet etching using,e.g., a diluted hydrofluoric acid solution is performed with respect tothe second insulating film 116 composed of the BPSG film to form thesecond insulating film 116 such that the portion of the secondinsulating film 116 overlying each of the memory gate electrodes 105 isthinner over each of the edge portions (peripheral portions) of thememory gate electrode 105 than over the middle portion thereof.

Thereafter, anisotropic dry etching is performed to form the upperportion of each of the memory gate electrodes 105 into a tapered orrounded protruding configuration, as shown in FIGS. 7A, 7B, and 7C.

Variation 2 of Embodiment 1

Referring to FIGS. 12A to 12C, a description will be given herein belowto a method for fabricating a semiconductor memory device according to asecond variation of the first embodiment of the present invention.

In contrast to the fabrication method according to the first embodimentwhich has used the atmospheric-pressure CVD as the deposition method forthe second insulating film 116 shown in FIGS. 5A to 5C, the fabricationmethod according to the second variation uses a reverse sputteringprocess such as argon sputtering.

Specifically, as shown in FIG. 12A, 12B, and 12C, when the secondinsulating film 116 composed of the BPSG film is deposited by using asputtering technology which covers the surface (target surface) of atarget material made of silicon oxide containing a phosphorus impurityand a boron impurity for a proper period of time to perform so-calledreverse sputtering, the second insulating film 116 having aconfiguration which is thinner over the edge portions of the uppersurface of each of the memory gate electrodes 105 than over the middleportion thereof can be formed.

As a result, the edge portions of the upper surface of each of thememory gate electrodes 105 can be exposed more easily in the subsequentetching step shown in FIGS. 6A to 6C. This allows the upper surface ofeach of the memory gate electrodes 105 to be exposed and each of theedge portions thereof to be etched easily into a tapered or roundedconfiguration as shown in FIGS. 7A to 7C.

In the first embodiment, the memory gate electrodes 105 in the firstactive region 103 and the logic gate electrode 112 in the second activeregion 104 are formed simultaneously in the same patterning step. Thisobviates the necessity to provide an extra margin between each of thememory gate electrodes 105 and the logic gate electrode 112 and anupper-layer contact formed thereon and thereby allows miniaturization.

Although the first embodiment has described the case where each of thememory elements formed in the first active region 103 is of the typewhich traps charge in the memory gate insulating film 110, it may alsobe of a type which has a floating gate electrode provided between thegate insulating film 110 and the gate electrode 105 and traps charge inthe provided floated gate electrode.

Although the first embodiment has deposited, in the insulating-filmforming step shown in FIGS. 5A and 5C, two types of insulating filmshaving different compositions such as the first insulating film 115 madeof silicon oxide and the second insulating film 116 made of BPSG andthereby formed the memory inter-gate insulating films 108 between thoseof the gate electrodes 105 which are adjacent in the directions in whichthe bit lines (the impurity diffusion layers 107) extend, they are notlimited thereto. It is also possible to stack three or more types ofinsulating films in layers. The reason for using two or more types ofinsulating films to form the memory inter-gate insulating films 108 isthat the memory gate electrodes 105 and the logic gate electrode 112 arepatterned in the same step in the first embodiment, as described above.Accordingly, if the memory inter-gate insulating films 108 which arenecessary between the individual memory gate electrodes 105 formed inthe first active region 103 as the memory region are deposited on thesemiconductor substrate 101, the insulating film for forming the memoryinter-gate insulating films 108 is deposited also on each of the logicgate electrode 112 and the impurity diffusion layers 114 in the secondactive region 104 as the logic region.

However, the insulating film for forming the memory inter-gateinsulating films that has been deposited on each of the logic gateelectrode 112 and the impurity diffusion layer 114 in the second activeregion 104 should be removed when the silicide layer 117 is formed oneach of the upper surfaces of the logic gate electrode 112 and theimpurity diffusion layers 114. Accordingly, the insulating film forforming the memory inter-gate insulating film can be removed preferablyfrom the second active region 104, while it is filled reliably in thefirst active region 103 even when the spacings between the gateelectrodes 105 are narrow. Such ease of filling and ease of removal canbe achieved more easily with a plurality of insulating films havingdifferent compositions than with an insulating film having a singlecomposition. By way of example, therefore, the first embodiment has usedsilicon oxide for the first insulating film 115 and BPSG for the secondinsulating film 116 and thereby allowed easy removal of the secondinsulating film 116 by wet etching, as shown in FIGS. 8A, 8B, and 8C.

Although the first embodiment has described the case where the memorygate electrodes 105 and the logic gate electrode 112 are formed in thesame step, the memory gate electrodes 105 and the logic gate electrode112 may also be formed in different steps if a sufficient margin can beprovided between each of the memory gate electrodes 105 and the logicgate electrode 112 and the upper-layer contact. This example will bedescribed as a second embodiment of the present invention.

Embodiment 2

The second embodiment of the present invention will be described withreference to the drawings.

FIG. 13 shows a partial plan configuration of a semiconductor memorydevice according to the second embodiment.

As shown in FIG. 13, the semiconductor memory device according to thefirst embodiment has a first active region 203 as a memory region inwhich a plurality of memory cells are provided and a second activeregion 204 as a logic region in which a logic element is provided. Thefirst and second active regions 203 and 204 are isolated from each otherby an element isolation insulating film formed selectively in an upperportion of a semiconductor substrate made of, e.g., silicon (Si). In thefirst active region 203, a plurality of memory transistors are providedas a matrix, while a logic transistor is provided in the second activeregion 204.

In the first active region 203, a plurality of memory gate electrodes205 are formed on the principal surface of the semiconductor substratewith respective memory gate insulating films interposed therebetween.Each of the memory gate insulating films is composed of a multilayerstructure having a lower gate insulating film made of silicon oxide, acharge accumulation film made of silicon nitride, and an upper gateinsulating film made of silicon oxide, which are formed successively onthe principal surface of the semiconductor substrate.

A plurality of memory transistors arranged in the gate length direction(the direction in which each of the gate electrodes 205 extends) havethe respective memory gate electrodes 205 which are formed in mutuallyconnected relation to constitute common gate electrodes 205. The commonmemory gate electrodes 205 form individual word lines. The upper surfaceof each of the memory gate electrodes 205 has edge portions (peripheralportions) each processed into a tapered or rounded cross-sectionalconfiguration. Silicide layers 209 are formed on the respectiveprocessed upper surfaces.

The cross section of the upper portion of the memory gate electrode 205in the direction perpendicular to the substrate surface is not limitedto a tapered configuration or a rounded configuration provided that theupper surface of the memory gate electrode 205 has a protrudingconfiguration which is higher in level at the middle portion than at theedge portions.

In the first active region 203 as the memory region, impurity diffusionlayers 207 are formed to extend in directions orthogonal to thedirections in which the word lines extend. Each of the impuritydiffusion layers 207 is formed to serve as the common source or drainregion of the memory transistors which are arranged in the directionorthogonal to the direction in which each of the word lines extends,while connecting the memory transistors to each other. These commonsource or drain regions form bit lines.

Thus, each of the memory transistors is constituted by the memory gateinsulating film, the memory gate electrode 205 having the silicide layer209 formed on the upper surface thereof, and the impurity diffusionlayers 207. Between the memory gate electrodes 205, memory inter-gateinsulating films 208 are formed.

In the second active region 204 as the logic region, on the other hand,the logic gate electrode 212 is formed over the principal surface of asemiconductor substrate 201 with a logic gate insulating film made ofsilicon oxide interposed therebetween. A sidewall insulating film 213 isformed on each of the respective side surfaces of the logic gateinsulating film and the logic gate electrode 212. In the second activeregion 204, the impurity diffusion layers each serving as the sourceregion or drain region are formed. The silicide layers 217 are formed onthe respective upper surfaces of the logic gate electrode 212 and theimpurity diffusion layers.

Thus, the logic transistor composed of a field-effect transistor isconstituted by the logic gate insulating film, the logic gate electrode212 having the silicide layer 217 formed on the upper portion thereof,and the impurity diffusion layers each having the silicide layer 217formed on the upper portion thereof.

A method for fabricating the semiconductor memory device according tothe second embodiment thus constituted will be described herein belowwith reference to the cross-sectional views of FIGS. 14A to 14C throughFIGS. 19A to 19C which illustrate individual process steps in the orderin which the fabrication process proceeds. Each of FIGS. 14A, 15A, 16A,17A, 18A, and 19A shows a cross-sectional configuration of the portioncorresponding to the line IXXa-IXXa of FIG. 13. Each of FIGS. 14B, 15B,16B, 17B, 18B, and 19B shows a cross-sectional configuration of theportion corresponding to the line IXXb-IXXb of FIG. 13. Each of FIGS.14C, 15C, 16C, 17C, 18C, and 19C shows a cross-sectional configurationof the portion corresponding to the line IXXc-IXXc of FIG. 13.

First, as shown in FIGS. 14A, 14B, and 14C, silicon oxide is buried intrenched portions each formed at a depth of about 300 nm in the upperportion of the semiconductor substrate 201 to form the isolationinsulating film 202, whereby the first active region 203 as the memoryregion and the second active region 204 as the logic region are formed.Subsequently, impurity ions, e.g., arsenic ions are implanted at a doseof about 5×10¹⁵/cm² into the specified portions of the first activeregion 203 with an acceleration voltage of about 50 KeV. Then, a thermalprocess in a nitrogen atmosphere at a temperature of, e.g., about 900°C. is performed for about 60 minutes with respect to the semiconductorsubstrate 200 into which the ions have been implanted to activate theimplanted arsenic ions, whereby the plurality of impurity diffusionlayers 207 serving as the source or drain regions of the memorytransistors are formed in the directions in which the bit lines extend.

Subsequently, a lower-layer silicon oxide film having a thickness of 10nm is formed by thermal oxidation on each of the first and second activeregions 203 and 204 of the semiconductor substrate 201. Then, anintermediate-layer silicon nitride film having a thickness of 7 nm andan upper-layer silicon oxide film having a thickness of 10 nm aredeposited successively by low-pressure CVD on the lower-layer siliconoxide film that has been formed. It is to be noted that the upper-layersilicon oxide film need not necessarily be formed

Subsequently, the intermediate-layer silicon oxide film and theupper-layer silicon oxide film are removed selectively from the secondactive region 204 by using a well-known etching technology. Then, apolycrystalline silicon film as a silicon-containing film having athickness of about 200 nm is deposited by low-pressure CVD on each ofthe first and second active regions 203 and 204. Subsequently, impurityions, e.g., phosphorus ions are implanted at a dose of about 2×10¹⁵/cm²into the deposited polycrystalline silicon films with an accelerationvoltage of about 10 KeV. Thereafter, a thermal process in a nitrogenatmosphere at a temperature of, e.g., about 800° C. is performed forabout 15 minutes with respect to the polycrystalline silicon films intowhich the ions have been implanted, thereby activating the implantedphosphorus ions.

Subsequently, in the first active region 203, the polycrystallinesilicon film, the upper-layer silicon oxide film, the intermediate-layersilicon nitride film, and the lower-layer silicon oxide film arepatterned successively by using well-known lithographic and etchingtechnologies to form the memory gate electrodes 205 each composed of thepolycrystalline silicon film and the memory gate insulating films 210each constituted by a multilayer structure having the upper gateinsulating film 210 c composed of the upper-layer silicon oxide film,the charge accumulation film 210 b composed of the intermediate-layersilicon nitride film, and the lower silicon oxide film 210 a composed ofthe lower-layer silicon oxide film.

Next, as shown in FIGS. 15A, 15B, and 15C, an insulating film 215composed of a silicon oxide film having a thickness of about 300 nm isdeposited by plasma CVD over the entire surface of the semiconductorsubstrate 201 including the plurality of memory gate electrodes 205, apolycrystalline silicon film, and the isolation insulating film 202 inthe first and second active regions 203 and 204.

Next, as shown in FIGS. 16A, 16B, and 16C, anisotropic etching includingan isotropic etching component is performed with respect to theinsulating film 215, thereby exposing the edge portions of the uppersurface of each of the memory gate electrodes 205 first. By way ofexample, the dry etching including an isotropic etching component isperformed under such conditions that tetra fluorocarbon (CF₄) at a flowrate of 100 cm³/min (at 0° C. and 1 atm) and oxygen (O₂) at a flow rateof 20 cm³/min (at 0° C. and 1 atm) are used as etching gases, power isadjusted to 100 W, and the pressure in a chamber is adjusted to 50 Pa.

Next, as shown in FIGS. 17A, 17B, and 17C, an etching process is furtherperformed under dry etching conditions including the lower etchingselectivity between the polycrystalline silicon and the insulating film215 made of silicon oxide, thereby exposing the upper surface of each ofthe memory gate electrodes 205, while etching each of the edge portionsof the upper surfaces of the memory gate electrodes 105 into a taperedor rounded configuration by using an over-etching process. By way ofexample, the dry etching with the low etching selectivity may beperformed appropriately by increasing the flow rate of oxygen among theforegoing etching conditions from 20 cm³/min (at 0° C. and 1 atm) to 50cm³/min (at 0° C. and 1 atm).

It is to be noted that each of the edge portions of the upper surfacesof the memory gate electrodes 205 is not limited to a tapered or roundedconfiguration provided that etching is performed in such a manner as toform the upper surface of each of the memory gate electrodes 205 into aprotruding portion which is higher in level at the middle portion thanat the edge portions (peripheral portions). By the sequence of etchingsteps, the insulating film 215 is left as the memory inter-gateinsulating films 208 on the regions of the principal surface of thesemiconductor substrate 201 which are located between the plurality ofmemory gate electrodes 205.

Thus, the fabrication method according to the second embodiment performsanisotropic etching including an isotropic etching component, as shownin FIGS. 16A, 16B, and 16C, and thereby allows the edge portions of theupper surface of each of the memory gate electrodes 205 to be exposedbefore the middle portion thereof is exposed. As a result, the edgeportions of the upper surface of the memory gate electrodes 205 areexposed to an etching gas for a longer period than the middle portionthereof, which allows the formation of each of the edge portions of theupper surfaces of the gate electrodes into a tapered or roundedconfiguration. Since the insulating film 215 exists between the adjacentmemory gate electrodes 205 in the sequence of etching steps, the regionsof the semiconductor substrate 201 which are located between the memorygate electrodes 205 are prevented from being grated by etching.Moreover, since the second active region 204 is covered with thepolycrystalline silicon film in the sequence of etching steps, theportion of the semiconductor substrate 201 included in the second activeregion 204 and the isolation insulating film 202 are prevented frombeing grated by etching.

Next, as shown in FIGS. 18A, 18B, and 18C, the polycrystalline siliconfilm and the lower-layer silicon oxide film are patterned successivelyin the second active region 204 so that the logic electrode 212 composedof the polycrystalline silicon film and a logic gate insulating film 211composed of the lower-layer silicon oxide film are formed. Subsequently,a silicon oxide film for forming sidewall insulating films having athickness of about 100 nm is deposited by low-pressure CVD over theentire surface including the plurality of memory gate electrodes 215,the logic gate electrode, and the isolation insulating film 202 in eachof the first and second active regions 203 and 204. At this time, thethickness of the portion of the silicon oxide film which is deposited oneach of the edge portions (tapered portions) of the upper surface ofeach of the memory gate electrodes 205 having the upper portions thereofeach formed into a protruding configuration, such as a taperedconfiguration, is equal to the thickness of the portion of the siliconoxide film which is deposited on the middle portion of the upper surfaceof the memory gate electrode 205.

Subsequently, an etch-back process corresponding to a depth of about 110nm is performed with respect to the deposited silicon oxide film,thereby forming the sidewall insulating film 213 on each of the sidesurfaces of the logic gate electrode 212. As a result, the silicon oxidefilm for forming the sidewall insulating film 213 is etched withoutremaining on the tapered portions of the upper surface of each of thememory gate electrodes 205 in the first active region 203 so that theupper portion of the memory gate electrode 205 is exposed. On the otherhand, an extremely small sidewall insulating film 206 remains on each ofthe memory inter-gate insulating films 208 between those of the memorygate electrodes 205 which are adjacent to each other.

By thus forming each of the edge portions of the upper surfaces of thememory gate electrodes 205 into a tapered or rounded configuration, thesilicon oxide film for forming the sidewall insulating film 213 on thelogic gate electrode 212 is removed by the etch-back process from theedge portions (peripheral portions) of the upper surface of each of thememory gate electrodes 205. As a result, the sidewall insulating films206 are prevented from being formed on the edge portions (peripheralportions) of the upper surface of each of the memory gate electrodes 205during the formation of the sidewall insulating film 213.

Subsequently, impurity ions, e.g., arsenic ions are implanted into thesemiconductor substrate 201 in the second active region 204 by using thelogic gate electrode 212 and the sidewall insulating film 213 as a maskand then a specified thermal process for activating the implantedimpurity ions is performed to form the impurity diffusion layer 214serving as the source region or drain region.

Next, as shown in FIGS. 19A, 19B, and 19C, the silicide layer 209 isformed by using a salicide technology on the tapered or rounded uppersurface as the protruding portion of each of the memory gate electrodes205 including the edge portions in the first active region 203. At thesame time, the silicide layer 217 is formed on each of the upper surfaceof the logic gate electrode 212 and the upper surface of the impuritydiffusion layer 214 in the second active region 204.

By the process described above, the semiconductor memory deviceaccording to the second embodiment can be obtained. Since a metal wiringstep, a protection-film forming step, a bonding-pad forming step, andthe like which are performed subsequently are well known, thedescription thereof will be omitted.

As described above, the second embodiment allows easy formation of thesilicide layer 209 on each of the memory gate electrodes 205 such thatthe length of the silicide layer 209 in the gate width direction islarger than the width of the gate by forming the upper surface of eachof the memory gate electrodes 205 into the protruding portion having theupwardly protruding middle portion in the first active region 203 as thememory region and then forming the silicide layer 209 on the protrudingportion. As a result, the contact area of the silicide layer 209 perunit length of the gate electrode increases and the resistance value perunit length of the memory gate electrode 205 (bar resistance) can bereduced. This allows the memory transistor to satisfy the requirementsfor further miniaturization and higher-speed operation.

Variation 1 of Embodiment 2

Referring to FIGS. 20A to 20C, a description will be given herein belowto a method for fabricating a semiconductor memory device according to afirst variation of the second embodiment of the present invention.

In contrast to the fabrication method according to the second embodimentwhich has used the anisotropic dry etching process including anisotropic etching component as the etching process for selectivelyexposing the edge portions of the upper surface of each of the memorygate electrodes 205 shown in FIGS. 16A to 16C, the first variationperforms isotropic etching and thereby forms the insulating film 215such that it is thinner at the portions thereof in the vicinity of theedge portions of the upper surface of the memory gate electrode 205 thanat the middle portion thereof.

Specifically, as shown in FIGS. 20A, 20B, and 20C, wet etching using,e.g., a diluted hydrofluoric acid solution is performed with respect tothe insulating film 215 made of silicon oxide to form the insulatingfilm 215 such that the portion of the insulating film 215 overlying eachof the memory gate electrodes 205 is thinner over each of the edgeportions (peripheral portions) of the memory gate electrode 205 thanover the middle portion thereof.

Thereafter, anisotropic dry etching is performed to form the upperportion of each of the memory gate electrodes 205 into a tapered orrounded protruding configuration, as shown in FIGS. 17A, 17B, and 17C.

Variation 2 of Embodiment 2

Referring to FIGS. 21A to 21C, a description will be given herein belowto a method for fabricating a semiconductor memory device according to asecond variation of the second embodiment of the present invention.

In contrast to the fabrication method according to the second embodimentwhich has used the atmospheric-pressure CVD as the deposition method forthe insulating film 215 shown in FIGS. 15A to 15C, the fabricationmethod according to the second variation uses a reverse sputteringprocess such as argon sputtering.

Specifically, as shown in FIG. 15A, 15B, and 15C, when the insulatingfilm 215 made of silicon oxide is deposited by using a sputteringtechnology which covers the surface (target surface) of a targetmaterial made of silicon oxide for a proper period of time to performso-called reverse sputtering, the insulating film 215 having aconfiguration which is thinner over the edge portions of the uppersurface of each of the memory gate electrodes 205 than over the middleportion thereof can be formed.

As a result, the edge portions of the upper surface of each of thememory gate electrodes 205 can be exposed more easily in the subsequentetching step shown in FIGS. 16A to 16C. This allows the upper surface ofeach of the memory gate electrodes 205 to be exposed and each of theedge portions thereof to be etched easily into a tapered or roundedconfiguration as shown in FIGS. 17A to 17C.

The second embodiment has performed the etching step for forming thememory inter-gate insulating films 208 shown in FIGS. 16A to 16C and 17Ato 17C, i.e., the step of forming the upper surface of each of thememory gate electrodes 205 into the protruding portion under suchconditions that the polycrystalline silicon film can also be etchedsimultaneously with the insulating film 215 made of silicon oxide and anetch rate for the polycrystalline silicon film is lower than an etchrate for the silicon oxide film. Accordingly, each of the edge portionsof the upper surfaces of the memory gate electrodes 205 that has beenexposed can be formed more effectively into a tapered configuration, asshown in FIGS. 16A to 16C.

Although the second embodiment has described the case where each of thememory elements formed in the first active region 203 is of the typewhich traps charge in the memory gate insulating film 210, it may alsobe of a type which has a floating gate electrode provided between thegate insulating film 210 and the gate electrode 205 and traps charge inthe provided floated gate electrode.

In the second embodiment, if the step of depositing the insulating film215 shown in FIG. 15 through the step of removing the insulating film215 to expose the upper surface of each of the memory gate electrodes205 and removing the edge portions of the upper surface of the memorygate electrode 205 shown in FIG. 17 are performed repeatedly, thetapered or rounded portion of each of the edge portions of the uppersurface of the memory gate electrode 205 can be increased in size. Thisallows the area of the silicide layer 209 to be increased moreeffectively.

Thus, the semiconductor memory device and the fabrication methodtherefor according to the present invention allow the region of thesilicide layer which is in contact with the upper surface of each of thegate electrodes to have a length in the gate width direction which islarger than the gate width so that the area of the silicide layer in thecross section of the gate electrode is larger than in the case where theupper surface of the gate electrode is flat. As a result, the resistancevalue per unit length of the gate electrode (bar resistance) is reducedand the memory transistor can satisfy the requirements for furtherminiaturization and higher-speed operation. Therefore, the semiconductormemory device and the fabrication method therefor according to thepresent invention are useful as a semiconductor memory device in which alogic region and a memory region having a diffusion wiring layerstructure are embedded and a fabrication method therefor.

1. A semiconductor memory device comprising a memory region in which aplurality of memory cells each including a memory transistor arearranged as a matrix using a plurality of bit lines and a plurality ofword lines intersecting each other, wherein a gate electrode of each ofthe memory transistors has an upper surface thereof formed into aprotruding portion which is higher in level at a middle portion than atan edge portion and a silicide layer is formed on an upper surface ofthe protruding portion of the gate electrode of the memory transistor.2. The semiconductor memory device of claim 1, wherein each of thememory transistors has an impurity diffusion layer serving as a sourceregion or drain region and also constituting a part of the correspondingone of the bit lines and has the gate electrode constituting a part ofthe corresponding one of the word lines.
 3. The semiconductor memorydevice of claim 1, wherein an inter-gate insulating film is formed on aregion of the substrate which is located between the respective gateelectrodes of the plurality of memory transistors.
 4. The semiconductormemory device of claim 1, further comprising: a logic region formed on aregion of the substrate other than the memory region and in which alogic transistor is disposed, wherein a sidewall insulating film isformed on each side surface of a gate electrode of the logic transistor.5. The semiconductor memory device of claim 4, wherein a silicide layeris formed on each of an upper surface of the gate electrode of the logictransistor and an exposed portion of an impurity diffusion layer servingas a source region or drain region of the logic transistor.
 6. Thesemiconductor memory device of claim 1, wherein each of the memorytransistors has a memory gate insulating film formed under the gateelectrode and the memory gate insulating film has a charge accumulationfilm.
 7. The semiconductor memory device of claim 6, wherein the memorygate insulating film is composed of a multilayer structure having alower-layer silicon oxide film and an upper-layer silicon nitride filmand the charge accumulation film is composed of the upper-layer siliconnitride film.
 8. The semiconductor memory device of claim 6, wherein thememory gate insulating film is composed of a multilayer structure havinga lower-layer silicon oxide film, an intermediate-layer silicon nitridefilm, and an upper-layer silicon oxide film and the charge accumulationfilm is composed of the intermediate-layer silicon nitride film.
 9. Thesemiconductor memory device of claim 1, wherein each of the memorytransistors has a memory gate insulating film formed under the gateelectrode and the memory gate insulating film is composed of amultilayer structure having a lower-layer silicon oxide film, anintermediate-layer silicon nitride film, and an upper-layer siliconoxide film and the intermediate-layer silicon nitride film is formed asa common intermediate-layer silicon nitride film connecting therespective memory gate insulating films of the plurality of memorytransistors to each other.
 10. The semiconductor memory device of claim2, wherein, of the plurality of memory transistors, each pair adjacentto each other in a direction in which each of the word lines extendsshare the common impurity diffusion layer serving as the source regionof one of the adjacent pair of memory transistors and also as the drainregion of the other thereof.
 11. The semiconductor memory device ofclaim 5, wherein the silicide layer on the gate electrode of each of thememory transistors and the silicide layer on the gate electrode of thelogic transistor have different cross-sectional configurations in adirection perpendicular to a surface of the substrate.
 12. A method forfabricating a semiconductor memory device having a memory region inwhich a plurality of memory cells each including a memory transistor arearranged as a matrix using a plurality of bit lines and a plurality ofword lines intersecting each other and a logic region in which a logictransistor is disposed, the method comprising the steps of: forming, inthe memory region, a first common impurity diffusion layer serving as asource region or drain region of each of the memory transistorscomposing those of the plurality of memory cells which are arranged in adirection in which each of the bit lines extends such that the firstcommon impurity diffusion layer extends in the direction in which thebit line extends; forming a memory gate insulating film on the memoryregion of the substrate, while forming a logic gate insulating film onthe logic region of the substrate; depositing a silicon-containing filmon each of the memory gate insulating film and the logic gate insulatingfilm; patterning the silicon-containing film in the memory region toform the common gate electrode of those of the plurality of memorytransistors which are arranged in a direction in which each of the wordlines extends such that the common gate electrode extends in thedirection in which the word line extends, while patterning thesilicon-containing film in the logic region to form the gate electrodeof the logic transistor; forming a sidewall insulating film on each sidesurface of the gate electrode of the logic transistor; forming, in thelogic region, a second impurity diffusion layer serving as a sourceregion or drain region of the logic transistor; forming a firstinsulating film on each of the memory region and the logic region andthen forming a second insulating film having a composition differentfrom a composition of the first insulating film on the first insulatingfilm that has been formed; successively performing etching with respectto the second insulating film and the first insulating film in thememory region to expose an edge portion of an upper surface of the gateelectrode of each of the plurality of memory transistors; after exposingthe edge portion of the upper surface of the gate electrode of each ofthe plurality of memory transistors, further performing etching toexpose the upper surface of the gate electrode of each of the pluralityof memory transistors and remove the edge portion of the upper surfaceof the gate electrode, while forming an inter-gate insulating filmcomposed at least of the first insulating film between the respectivegate electrodes of those of the memory transistors which are adjacent toeach other in the direction in which each of the bit lines extends;successively performing etching with respect to the second insulatingfilm and the first insulating film in the logic region to expose each ofan upper surface of the gate electrode of the logic transistor and anupper surface of the second impurity diffusion layer; and forming asilicide layer on each of the upper surface of the gate electrode ofeach of the plurality of memory transistors from which the edge portionhas been removed, the upper surface of the gate electrode of the logictransistor, and an exposed portion of the second impurity diffusionlayer.
 13. The method of claim 12, wherein the memory gate insulatingfilm has a charge accumulation film.
 14. The method of claim 13, whereinthe memory gate insulating film is composed of a multilayer structurehaving a lower-layer silicon oxide film and an upper-layer siliconnitride film and the charge accumulation film is composed of theupper-layer silicon nitride film.
 15. The method of claim 13, whereinthe memory gate insulating film is composed of a multilayer structurehaving a lower-layer silicon oxide film, an intermediate-layer siliconnitride film, and an upper-layer silicon oxide film and the chargeaccumulation film is composed of the intermediate-layer silicon nitridefilm.
 16. The method of claim 12, wherein the etching performed withrespect to the second and first insulating films in the step of exposingthe edge portion of the upper surface of the gate electrode of each ofthe plurality of memory transistors is isotropic etching.
 17. The methodof claim 12, wherein the etching performed with respect to the secondand first insulating films after exposing the edge portion of the uppersurface of the gate electrode of each of the plurality of memorytransistors is anisotropic etching.
 18. The method of claim 12, whereinthe etching of the second and first insulating films is performed undersuch a condition that an etch rate for each of the first and secondinsulating films is higher than an etch rate for the silicon-containingfilm.
 19. The method of claim 12, wherein the second insulating film isformed by reverse sputtering.
 20. A method for fabricating asemiconductor memory device having a memory region in which a pluralityof memory cells each including a memory transistor are arranged as amatrix using a plurality of bit lines and a plurality of word linesintersecting each other and a logic region in which a logic transistoris disposed, the method comprising the steps of: forming, in the memoryregion, a first common impurity diffusion layer serving as a sourceregion or drain region of each of the memory transistors composing thoseof the plurality of memory cells which are arranged in a direction inwhich each of the bit lines extends such that the first common impuritydiffusion layer extends in the direction in which the bit line extends;forming a memory gate insulating film on the memory region of thesubstrate, while forming a logic gate insulating film on the logicregion of the substrate; depositing a silicon-containing film on each ofthe memory gate insulating film and the logic gate insulating film;patterning the silicon-containing film in the memory region to form thecommon gate electrode of those of the plurality of memory transistorswhich are arranged in a direction in which each of the word linesextends such that the common gate electrode extends in the direction inwhich the word line extends; forming an insulating film on each of thememory region and the logic region; performing etching with respect tothe insulating film on the memory region to expose an edge portion of anupper surface of the gate electrode of each of the plurality of memorytransistors; after exposing the edge portion of the upper surface of thegate electrode, further performing etching to expose the upper surfaceof the gate electrode of each of the plurality of memory transistors andremove the edge portion of the upper surface of the gate electrode,while forming an inter-gate insulating film composed of the insulatingfilm between the respective gate electrodes of those of the memorytransistors which are adjacent to each other in the direction in whicheach of the bit lines extends; patterning the silicon-containing film inthe logic region to form the gate electrode of the logic transistor;forming a sidewall insulating film on each side surface of the gateelectrode of the logic transistor; forming, in the logic region, asecond impurity diffusion layer serving as a source region or drainregion of the logic transistor; and forming a silicide layer on each ofthe upper surface of the gate electrode of each of the plurality ofmemory transistors from which the edge portion has been removed, theupper surface of the gate electrode of the logic transistor, and anexposed portion of the second impurity diffusion layer.
 21. The methodof claim 20, wherein the memory gate insulating film has a chargeaccumulation film.
 22. The method of claim 21, wherein the memory gateinsulating film is composed of a multilayer structure having alower-layer silicon oxide film and an upper-layer silicon nitride filmand the charge accumulation film is composed of the upper-layer siliconnitride film.
 23. The method of claim 21, wherein the memory gateinsulating film is composed of a multilayer structure having alower-layer silicon oxide film, an intermediate-layer silicon nitridefilm, and an upper-layer silicon oxide film and the charge accumulationfilm is composed of the intermediate-layer silicon nitride film.
 24. Themethod of claim 20, wherein the etching performed with respect to theinsulating film in the step of exposing the edge portion of the uppersurface of the gate electrode of each of the plurality of memorytransistors is isotropic etching.
 25. The method of claim 20, whereinthe etching performed with respect to the insulating film after exposingthe edge portion of the upper surface of the gate electrode of each ofthe plurality of memory transistors is anisotropic etching.
 26. Themethod of claim 20, wherein the etching of the insulating film isperformed under such a condition that an etch rate for the insulatingfilm is higher than an etch rate for the silicon-containing film. 27.The method of claim 20, wherein the insulating film is formed by reversesputtering.